Physical Properties of 5 Root Canal Sealers

Introduction: The aim of this study was to evaluate the pH change, viscosity and other physical properties of 2 novel root canal sealers (MTA Fillapex and Endosequence BC) in comparison with 2 epoxy resin-based sealers (AH Plus and ThermaSeal), a silicone-based sealer (GuttaFlow), and a zinc oxide-eugenol-based sealer (Pulp Canal Sealer).

Methods: ISO 6876/2001 specifications were followed. The pH change of freshly mixed and set sealers was evaluated during periods of 1 day and 5 weeks, respectively. The viscosity was investigated at different injection rates (72, 10, and 5 mm/min) at room temperature by using a syringe-based system that was based on the Instron 3360 series universal testing system.

Results: The flow, dimensional change, solubility, and film thickness of all the tested sealers were in agreement with ISO 6876/2001 recommendations. The MTA Fillapex sealer exhibited a higher flow than the Endosequence BC sealer (P < .05). The MTA Fillapex and Endosequence BC sealers showed the highest film thicknesses among the tested samples. The Endosequence BC sealer exhibited the highest value of solubility, which was in accordance with 3% mass fraction recommended by the ISO 6876/2001, and showed an acceptable dimensional change. The MTA Fillapex and Endosequence BC sealers presented an alkaline pH at all times. The pH of fresh samples of the AH Plus and ThermaSeal sealers was alkaline at first but decreased significantly after 24 hours. The viscosity of the tested sealers increased with the decreased injection rates.

Conclusions: The tested sealers were pseudoplastic according to their viscosities as determined in this study. The MTA Fillapex and Endosequence BC sealers each possessed comparable flow and dimensional stability but higher film thickness and solubility than the other sealers tested.