Fatigue and Failure Mode Analyses of Glass Infiltrated 5Y-PSZ Bonded Onto Dentin Analogues

Overview

Journal Sci Rep

Specialty Science

Date 2024 Jun 10

PMID 38858417

Authors

Jonas Vinicius Meireles Rodrigues

Amir Mohidin Demachkia

Rita Adriana Souza da Silva de Assis

Mariana Marques Gomes

Tiago Moreira Bastos Campos

Kiara Serafini Dapieve

Luiz Felipe Valandro

Renata Marques de Melo

Affiliations

Soon will be listed here.

Abstract

The purpose of this study was to evaluate the fatigue survival of 5Y-PSZ zirconia infiltrated with an experimental glass and bonded onto dentin analogues. Disc-shaped specimens of a 5Y-PSZ (Katana UTML Kuraray Noritake) were cemented onto dentin analogs (NEMA G10) and divided into four groups (n = 15): Zctrl Group (control, without infiltration); Zglz Group (Glaze, compression surface); Zinf-comp Group (Experimental Glass, compression surface); Zinf-tens Group (Experimental Glass, tension surface). Surface treatments were varied. Cyclic fatigue loading, oblique transillumination, stereomicroscope examination, and scanning electron microscopy were performed. Fatigue data were analyzed (failure load and number of cycles) using survival analysis (Kaplan-Meier and Log-Rank Mantel-Cox). There was no statistically significant difference in fatigue survival between the Zglz, Zctrl, and Zinf-comp groups. The Zinf-tens group presented a significantly higher failure load when compared to the other groups and exhibited a different failure mode. The experimental glass effectively infiltrated the zirconia, enhancing structural reliability, altering the failure mode, and improving load-bearing capacity over more cycles, particularly in the group where the glass was infiltrated into the tensile surface of the zirconia. Glass infiltration into 5Y-PSZ zirconia significantly enhanced structural reliability and the ability to withstand loads over an increased number of cycles. This approach has the potential to increase the durability of zirconia restorations, reducing the need for replacements and save time and resources, promoting efficiency in clinical practice.

References

Kim S, Oh N, Pang N, Jung B . The effect of surface treatment and low-temperature degradation on flexural strength of additive manufactured zirconia. J Mech Behav Biomed Mater. 2023; 148:106167. DOI: 10.1016/j.jmbbm.2023.106167. View

Mao L, Kaizer M, Zhao M, Guo B, Song Y, Zhang Y . Graded Ultra-Translucent Zirconia (5Y-PSZ) for Strength and Functionalities. J Dent Res. 2018; 97(11):1222-1228. PMC: 6151910. DOI: 10.1177/0022034518771287. View

Zhang Y, Lawn B . Novel Zirconia Materials in Dentistry. J Dent Res. 2017; 97(2):140-147. PMC: 5784474. DOI: 10.1177/0022034517737483. View

Aurelio I, Marchionatti A, Montagner A, May L, Soares F . Does air particle abrasion affect the flexural strength and phase transformation of Y-TZP? A systematic review and meta-analysis. Dent Mater. 2016; 32(6):827-45. DOI: 10.1016/j.dental.2016.03.021. View

Sulaiman T, Abdulmajeed A, Shahramian K, Lassila L . Effect of different treatments on the flexural strength of fully versus partially stabilized monolithic zirconia. J Prosthet Dent. 2017; 118(2):216-220. DOI: 10.1016/j.prosdent.2016.10.031. View

Prochnow C, Venturini A, Guilardi L, Pereira G, Burgo T, Bottino M . Hydrofluoric acid concentrations: Effect on the cyclic load-to-failure of machined lithium disilicate restorations. Dent Mater. 2018; 34(9):e255-e263. DOI: 10.1016/j.dental.2018.06.028. View

Hajhamid B, Alfrisany N, Somogyi-Ganss E . The effect of accelerated aging on crystalline structures and optical properties of different monolithic zirconia: A qualitative systematic review. Dent Mater. 2022; 38(4):569-586. DOI: 10.1016/j.dental.2022.02.005. View

Pereira G, Guilardi L, Dapieve K, Kleverlaan C, Rippe M, Valandro L . Mechanical reliability, fatigue strength and survival analysis of new polycrystalline translucent zirconia ceramics for monolithic restorations. J Mech Behav Biomed Mater. 2018; 85:57-65. DOI: 10.1016/j.jmbbm.2018.05.029. View

Rodrigues C, Dhital S, Kim J, May L, Wolff M, Zhang Y . Residual stresses explaining clinical fractures of bilayer zirconia and lithium disilicate crowns: A VFEM study. Dent Mater. 2021; 37(11):1655-1666. PMC: 8578443. DOI: 10.1016/j.dental.2021.08.019. View

10.

Vardhaman S, Borba M, Kaizer M, Kim D, Zhang Y . Wear behavior and microstructural characterization of translucent multilayer zirconia. Dent Mater. 2020; 36(11):1407-1417. PMC: 7969479. DOI: 10.1016/j.dental.2020.08.015. View

11.

Ramos G, Ramos N, Alves L, Kaizer M, Borges A, Campos T . Failure probability and stress distribution of milled porcelain-zirconia crowns with bioinspired/traditional design and graded interface. J Mech Behav Biomed Mater. 2021; 119:104438. DOI: 10.1016/j.jmbbm.2021.104438. View

12.

Smielak B, Klimek L . Effect of hydrofluoric acid concentration and etching duration on select surface roughness parameters for zirconia. J Prosthet Dent. 2015; 113(6):596-602. DOI: 10.1016/j.prosdent.2015.01.001. View

13.

Pereira R, Campos T, Bonfante E, Thim G . A comparative study of mechanical properties of yttria stabilized zirconia monolithic and bilayer configuration for dental application. J Mech Behav Biomed Mater. 2023; 148:106160. DOI: 10.1016/j.jmbbm.2023.106160. View

14.

Campos T, Dos Santos C, Martins Alves L, Benalcazar-Jalkh E, Strazzi-Sahyon H, Bergamo E . Minimally processed recycled yttria-stabilized tetragonal zirconia for dental applications: Effect of sintering temperature on glass infiltration. J Mech Behav Biomed Mater. 2023; 150:106311. DOI: 10.1016/j.jmbbm.2023.106311. View

15.

Koenig V, Douillard T, Chevalier J, Amiard F, Lamy de la Chapelle M, Le Goff S . Intraoral low-temperature degradation of monolithic zirconia dental prostheses: 5-year results of a prospective clinical study with ex vivo monitoring. Dent Mater. 2023; 40(2):198-209. DOI: 10.1016/j.dental.2023.11.008. View

16.

Muhlemann S, Lakha T, Jung R, Hammerle C, Benic G . Prosthetic outcomes and clinical performance of CAD-CAM monolithic zirconia versus porcelain-fused-to-metal implant crowns in the molar region: 1-year results of a RCT. Clin Oral Implants Res. 2020; 31(9):856-864. DOI: 10.1111/clr.13631. View

17.

Dartora G, Pereira G, de Carvalho R, Zucuni C, Valandro L, Cesar P . Comparison of endocrowns made of lithium disilicate glass-ceramic or polymer-infiltrated ceramic networks and direct composite resin restorations: fatigue performance and stress distribution. J Mech Behav Biomed Mater. 2019; 100:103401. DOI: 10.1016/j.jmbbm.2019.103401. View

18.

Pilecco R, Machry R, Ribeiro V, Dal Piva A, Tribst J, Kleverlaan C . Impact of try-in paste removal on the fatigue behavior of bonded lithium disilicate ceramics. J Mech Behav Biomed Mater. 2024; 151:106394. DOI: 10.1016/j.jmbbm.2024.106394. View

19.

Toyama D, Martins Alves L, Ramos G, Campos T, de Vasconcelos G, Borges A . Bioinspired silica-infiltrated zirconia bilayers: Strength and interfacial bonding. J Mech Behav Biomed Mater. 2018; 89:143-149. DOI: 10.1016/j.jmbbm.2018.09.013. View

20.

Campos T, Ramos N, Machado J, Bottino M, Souza R, Melo R . A new silica-infiltrated Y-TZP obtained by the sol-gel method. J Dent. 2016; 48:55-61. DOI: 10.1016/j.jdent.2016.03.004. View