The Potential of Galactomannan from Caesalpinia Ferrea on Erosive Dentin Wear Reduction in Vitro

Gels containing juca seed galactomannan (JSG) were evaluated for their potential to prevent the progression of dentin erosive wear in an in vitro study with four experimental groups (n = 9). The treatments included distilled water (DW), 0.05% stannous fluoride (121 ppm F), and 0.5% or 1% JSG. The specimens underwent a cycle (3 times/day) consisting of immersion in 1% citric acid (5 minutes), treatment (5 minutes), and artificial saliva exposure (2 hours/overnight) for 5 days. Surface changes were assessed using mechanical profilometry (wear), scanning electron microscopy (SEM), and energy-dispersive X-ray spectroscopy (EDS). The data were analyzed using ANOVA followed by Tukey's post-test (p < 0.05). The negative control group exhibited the highest wear (6.0 µm ± 3.5), significantly differing from the group treated with 0.05% stannous fluoride gel (p = 0.007), which showed less dentin loss. The groups treated with 0.5% and 1% JSG showed results similar to the negative control (p = 0.661; p = 0.212, respectively) and the stannous fluoride group (p = 0.103; p = 0.379, respectively). In the SEM images, the specimen treated with stannous fluoride showed obliterated tubules, while the JSG gels formed crystals on the dentin surface, as confirmed by the presence of oxygen and calcium in the EDS analysis. Although the JSG gels showed similar results to the stannous fluoride, did not exhibit superior efficacy at the tested concentrations.