Repair of Bulk-Fill and Nanohybrid Resin Composites: Effect of Surface Conditioning, Adhesive Promoters, and Long-Term Aging

Overview
Publisher MDPI
Date 2022 Jul 9
PMID 35806811
Authors
Affiliations
Soon will be listed here.
Abstract

The aim of the study was to investigate the effect of different repair procedures on the repair bond strength of bulk-fill and nanohybrid resin composites after different aging periods. The resin composite blocks (8 × 8 × 4 mm3) were prepared from a bulk-fill (reliaFIL Bulk) and a nanohybrid (reliaFIL LC) resin composite and grouped according to aging duration (6 months, 1 year, and 2 years). Following aging, the blocks were assigned to different surface treatments; air-abrasion with aluminum oxide powder, roughening with a diamond bur, and no treatment. After cleansing with phosphoric acid, a silane layer (Porcelain Primer) was applied on the surface of half of the specimens in each group. The specimens were subdivided into two groups (n = 5): Scotchbond Universal (3M Oral Care) and All-Bond Universal (Bisco). The blocks were repaired with the nanohybrid composite (8 × 8 × 8 mm 3). The repaired specimens were stored in distilled water (37 °C/24 h) and segmented into beams. Half of the beams were immediately subjected to microtensile μTBS testing (1 mm/min), while the other half was stored in distilled water (37 °C) for 6 months before testing. Failure modes were analyzed using stereomicroscope and SEM. Statistical analyses were performed with ANOVA and least significant difference tests (LSD) tests (p = 0.05). The extension of aging periods (6 months, 1 year, and 2 years) reduced the repair bond strength in some groups for both resin composites (p < 0.05). The air-abrasion and bur roughening improved the repair bond strength (p < 0.05). The silane application did not influence the repair bond strength and durability (p > 0.05). There was no difference among the universal adhesives in the same surface treatment groups (p > 0.05). The mechanical roughening treatments are necessary for the repair of resin composite. The universal adhesives might be used for the repair of resin composites regardless of silane content without prior silane application.

Citing Articles

The Effect of Mechanical Alteration on Repair Bond Strength of S-PRG-Filler-Based Resin Composite Materials.

Islam M, Aryal A C S, El Bahra S, Abuhajjeh A, Al Mofleh A, Padmanabhan V Polymers (Basel). 2024; 16(11).

PMID: 38891435 PMC: 11174450. DOI: 10.3390/polym16111488.


The efficacy of Er,Cr:YSGG laser and contemporary universal adhesive systems on composite resin repair bond strength: an in vitro study.

Dogan E, Cevval Ozkocak B Odontology. 2024; 112(4):1197-1208.

PMID: 38568323 DOI: 10.1007/s10266-024-00932-2.


Effect of brushing simulation on the wear behavior of repaired CAD-CAM restorations.

Soares P, Dal Piva A, Pereira G, Valandro L, Rippe M, Feilzer A Int Dent J. 2024; 74(5):999-1005.

PMID: 38461097 PMC: 11561493. DOI: 10.1016/j.identj.2024.02.012.


Mechanical Behavior of Repaired Monolithic Crowns: A 3D Finite Element Analysis.

Soares P, Rosa L, Pereira G, Valandro L, Rippe M, Dal Piva A Dent J (Basel). 2023; 11(11).

PMID: 37999018 PMC: 10670502. DOI: 10.3390/dj11110254.


Effect of Different Surface Treatments on the Long-Term Repair Bond Strength of Aged Methacrylate-Based Resin Composite Restorations: A Systematic Review and Network Meta-analysis.

Hadilou M, Dolatabadi A, Ghojazadeh M, Hosseinifard H, Alizadeh Oskuee P, Pournaghi Azar F Biomed Res Int. 2023; 2022:7708643.

PMID: 37964860 PMC: 10643039. DOI: 10.1155/2022/7708643.


References
1.
Flury S, Dulla F, Peutzfeldt A . Repair bond strength of resin composite to restorative materials after short- and long-term storage. Dent Mater. 2019; 35(9):1205-1213. DOI: 10.1016/j.dental.2019.05.008. View

2.
Loomans B, Cardoso M, Opdam N, Roeters F, De Munck J, Huysmans M . Surface roughness of etched composite resin in light of composite repair. J Dent. 2011; 39(7):499-505. DOI: 10.1016/j.jdent.2011.04.007. View

3.
Van Ende A, de Munck J, Lise D, Van Meerbeek B . Bulk-Fill Composites: A Review of the Current Literature. J Adhes Dent. 2017; 19(2):95-109. DOI: 10.3290/j.jad.a38141. View

4.
Valente L, Silva M, Fonseca A, Munchow E, Isolan C, Moraes R . Effect of Diamond Bur Grit Size on Composite Repair. J Adhes Dent. 2015; 17(3):257-63. DOI: 10.3290/j.jad.a34398. View

5.
Costa T, Ferreira S, Klein-Junior C, Loguercio A, Reis A . Durability of surface treatments and intermediate agents used for repair of a polished composite. Oper Dent. 2010; 35(2):231-7. DOI: 10.2341/09-216-L. View