Mussel-Inspired Polydopamine-Functionalized Graphene As a Conductive Adhesion Promoter and Protective Layer for Silver Nanowire Transparent Electrodes

For the scalable fabrication of transparent electrodes and optoelectronic devices, excellent adhesion between the conductive films and the substrates is essential. In this work, a novel mussel-inspired polydopamine-functionalized graphene/silver nanowire hybrid nanomaterial for transparent electrodes was fabricated in a facile manner. Graphene oxide (GO) was functionalized and reduced by polydopamine while remaining stable in water without precipitation. It is shown that the polydopamine-functionalized GO (PFGO) film adhered to the substrate much more easily and more uniformly than the GO film. The PFGO film had a sheet resistance of ∼3.46 × 10(8) Ω/sq and a transparency of 78.2%, with excellent thermal and chemical stability; these characteristics are appropriate for antistatic coatings. Further reduced PFGO (RPFGO) as a conductive adhesion promoter and protective layer for the Ag nanowire (AgNW) significantly enhanced the adhesion force between AgNW networks and the substrate. The RPFGO-AgNW electrode was found to have a sheet resistance of 63 Ω/sq and a transparency of 70.5%. Moreover, the long-term stability of the RPFGO-AgNW electrode was greatly enhanced via the effective protection of the AgNW by RPFGO. These solution-processed antistatic coatings and electrodes have tremendous potential in the applications of optoelectronic devices as a result of their low production cost and facile processing.