Wafer-Scale Integration of Inverted Nanopyramid Arrays for Advanced Light Trapping in Crystalline Silicon Thin Film Solar Cells

Overview
Publisher Springer
Specialty Biotechnology
Date 2016 Apr 14
PMID 27071681
Citations 4
Authors
Affiliations
Soon will be listed here.
Abstract

Crystalline silicon thin film (c-Si TF) solar cells with an active layer thickness of a few micrometers may provide a viable pathway for further sustainable development of photovoltaic technology, because of its potentials in cost reduction and high efficiency. However, the performance of such cells is largely constrained by the deteriorated light absorption of the ultrathin photoactive material. Here, we report an efficient light-trapping strategy in c-Si TFs (~20 μm in thickness) that utilizes two-dimensional (2D) arrays of inverted nanopyramid (INP) as surface texturing. Three types of INP arrays with typical periodicities of 300, 670, and 1400 nm, either on front, rear, or both surfaces of the c-Si TFs, are fabricated by scalable colloidal lithography and anisotropic wet etch technique. With the extra aid of antireflection coating, the sufficient optical absorption of 20-μm-thick c-Si with a double-sided 1400-nm INP arrays yields a photocurrent density of 39.86 mA/cm(2), which is about 76 % higher than the flat counterpart (22.63 mA/cm(2)) and is only 3 % lower than the value of Lambertian limit (41.10 mA/cm(2)). The novel surface texturing scheme with 2D INP arrays has the advantages of excellent antireflection and light-trapping capabilities, an inherent low parasitic surface area, a negligible surface damage, and a good compatibility for subsequent process steps, making it a good alternative for high-performance c-Si TF solar cells.

Citing Articles

Design and Optimization of a Self-Protected Thin Film c-Si Solar Cell against Reverse Bias.

Saif O, Zekry A, Shaker A, Abouelatta M, Alanazi T, Saeed A Materials (Basel). 2023; 16(6).

PMID: 36984391 PMC: 10059038. DOI: 10.3390/ma16062511.


Thermal conductivity of poly(3,4-ethylenedioxythiophene) films engineered by oxidative chemical vapor deposition (oCVD).

Smith P, Su L, Gong W, Nakamura N, Reeja-Jayan B, Shen S RSC Adv. 2022; 8(35):19348-19352.

PMID: 35541006 PMC: 9080664. DOI: 10.1039/c8ra03302a.


Manipulation and Applications of Hotspots in Nanostructured Surfaces and Thin Films.

Zhao X, Wen J, Zhu A, Cheng M, Zhu Q, Zhang X Nanomaterials (Basel). 2020; 10(9).

PMID: 32858806 PMC: 7557400. DOI: 10.3390/nano10091667.


Excellent Light Confinement of Hemiellipsoid- and Inverted Hemiellipsoid-Modified Semiconductor Nanowire Arrays.

Chen X, Wang J, Shao P, Liu Q, Liu D, Chen Q Nanoscale Res Lett. 2018; 13(1):236.

PMID: 30112714 PMC: 6093829. DOI: 10.1186/s11671-018-2659-2.

References
1.
Zhu J, Hsu C, Yu Z, Fan S, Cui Y . Nanodome solar cells with efficient light management and self-cleaning. Nano Lett. 2009; 10(6):1979-84. DOI: 10.1021/nl9034237. View

2.
Yahaya N, Yamada N, Kotaki Y, Nakayama T . Characterization of light absorption in thin-film silicon with periodic nanohole arrays. Opt Express. 2013; 21(5):5924-30. DOI: 10.1364/OE.21.005924. View

3.
Brongersma M, Cui Y, Fan S . Light management for photovoltaics using high-index nanostructures. Nat Mater. 2014; 13(5):451-60. DOI: 10.1038/nmat3921. View

4.
Mavrokefalos A, Han S, Yerci S, Branham M, Chen G . Efficient light trapping in inverted nanopyramid thin crystalline silicon membranes for solar cell applications. Nano Lett. 2012; 12(6):2792-6. DOI: 10.1021/nl2045777. View

5.
Wang S, Weil B, Li Y, Wang K, Garnett E, Fan S . Large-area free-standing ultrathin single-crystal silicon as processable materials. Nano Lett. 2013; 13(9):4393-8. DOI: 10.1021/nl402230v. View