Synthesis, Structural and Hydrogenation Properties of Mg-rich MgH2-TiH2 Nanocomposites Prepared by Reactive Ball Milling Under Hydrogen Gas

MgH(2)-TiH(2) nanocomposites have been obtained by reactive ball milling of elemental powders under 8 MPa of hydrogen pressure. The composites consist of a mixture of β-rutile MgH(2), γ-orthorhombic high pressure MgH(2) and ε-tetragonal TiH(2) phases with nanosized crystallites ranging from 4 to 12 nm. In situ hydrogen absorption curves on milling reveal that nanocomposite formation occurs in less than 50 min through the consecutive synthesis of the TiH(2) and MgH(2) phases. The abrasive and catalytic properties of TiH(2) speed up the formation of the MgH(2) phase. Thermodynamic, kinetic and cycling hydrogenation properties have been determined for the 0.7MgH(2)-0.3TiH(2) composite and compared to nanometric MgH(2). Only the MgH(2) phase desorbs hydrogen reversibly at moderate temperature (523 to 598 K) and pressure (10(-3) to 1 MPa). The presence of TiH(2) does not modify the thermodynamic properties of the Mg/MgH(2) system. However, the MgH(2)-TiH(2) nanocomposite exhibits outstanding kinetic properties and cycling stability. At 573 K, H-sorption takes place in less than 100 s. This is 20 times faster than for a pure nanometric MgH(2) powder. We demonstrate that the TiH(2) phase inhibits grain coarsening of Mg, which allows extended nucleation of the MgH(2) phase in Mg nanoparticles before a continuous and blocking MgH(2) hydride layer is formed. The low crystallinity of the TiH(2) phase and its hydrogenation properties are also compatible with a gateway mechanism for hydrogen transfer from the gas phase to Mg. Mg-rich MgH(2)-TiH(2) nanocomposites are an excellent media for hydrogen storage at moderate temperatures.