PH- and Temperature-Responsive P(DMAEMA-GMA)-Alginate Semi-IPN Hydrogels Formed by Radical and Ring-Opening Polymerization for Aminophylline Release

A novel poly((2-dimethylamino) ethyl methacrylate-glycidyl methacrylate)-alginate (P(DMAEMA-GMA)alginate) semi-IPN hydrogel was synthesized via radical polymerization of the double bonds and ring-opening of the epoxy groups without using catalyst and cross-linker. (1)H-NMR, FT-IR and DSC data were consistent with the expected structures for the hydrogels. The interior morphology of the hydrogels was also investigated by SEM. The swelling ratio and compressive strength of the hydrogels were measured. The semi-IPN hydrogel had pH and temperature sensitivity, and pH-sensitive points of all hydrogels were found to be at pH 5.0. The release behavior of the model drug, aminophylline, was found to be dependent on the hydrogel composition and environment pH, which manifests that these materials have potential applications as intelligent drug carriers.